CW-1 Steel Round Bar, CW-1 Steel Round Bar Manufacturers, CW-1 Steel Suppliers, CW-1 Stockist, CW-1 Steel Dealers, CW-1 Steel Distributors, CW-1 Wholesalers, CW-1 Steel Traders, CW-1 Steel Square Distributors, CW-1 Steel Flat Bar, CW-1 Steel Companies Near me.
 
Grade Introduction:
The high-quality USA AISI CW-1 material is one of the more steel grades we supply, W-Ta-Nb-Ti-Co class carbide. CW-1 is our main production grade, which has been approved by customers in many countries since its initial production, including our CW-1 round bars, flat bar, forgings, fasteners, tubes, wires, strips, sheets & Plates, as well as a variety of profiles, professional high precision auto-lathe processing manufacturer of clinching fasteners, axes, standoffs, screws, studs, nuts, bolt, OEM parts and special-shaped turning parts the state of delivery includes quenched and tempered, annealed, machined semi-finished products, we also have strict management of the packaging, to avoid material damage from transportation. We are the best supplier of CW-1 materials, and we are willing to develop together with customers from all over the world.
 
Grade Application:
  • Plastic injection molds and inserts
  • Plastic injection and extrusion feed screws
  • Non-return valve components
  • Pelletizing equipment
  • Nozzles
  • Gate and nozzle inserts.
  • Industrial knives, slitters, and cutters.
  • Wear-resistant specialty cutlery.
  • Wear components for food and chemical processing.
  • Bearings, bushings, valves, rolls.
  • Gear pumps.
 
Equivalent grades:
MaterialStandardCountry
CW-12MWAISIUSA
 
Addition to other grades:
MS, EN1A, EN3B, EN8, EN8D, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, HCHCR, OHNS, D2, D3, H-11, H-13, M2, M35, M42, 2714, SKD-11, P20, P20+S, P20+Ni, SCM 420, ASTM SA-36, ASTM SA-105, SAE 1018, SAE 1020, SAE 4140, SAE 8620, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE 52100, S40C, S355J2G3.
 
Our Supply Range:
 
Price List:
 
People also search as:
CW-1, CW-1 Steel, CW-1 Chemical composition, CW-1 Mechanical properties, CW-1 Equivalent Grades, CW-1 Steel plate, CW-1 Steel sheet, CW-1 Manufacturers, CW-1 Suppliers, CW-1 Dealers, CW-1 Stockist, CW-1 Distributors, CW-1 Wholesalers, CW-1 Traders.
 
Chemical composition:
The following table shows the chemical composition of CW-1 steel:
C ≤Si ≤Mn ≤P ≤S ≤Cr ≤Ni ≤
6.7
MoAIWNbTiVTa
68.91.66.75.4
NCoPbBOther
10.7
 
Mechanical Properties:
Properties Conditions
T (°C)Treatment
Density (×1000 kg/m3)7.7-8.0325
Poisson’s Ratio0.27-0.3025
Elastic Modulus (GPa)190-21025
Tensile Strength (Mpa)115825oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa)1034
Elongation (%)15
Reduction in Area (%)53
Hardness (HB)33525oil quenched, fine grained, tempered at 425°C
 
Hardness:
335
 
Heat treatment:
1565°C – 1756°C
 
Hardening:
Micro-Melt 420-CW tool steel should be heat treated using proper precautions to prevent decarburization. First preheat to 1500/1550°F (816/843°C), equalize, and transfer to a furnace maintained at the desired hardening temperature. Austenitize: 1950-2150°F (1066-1175°C) and hold time at temperature for 20-30 minutes. Note: For larger section sizes, fan air cooling or step quenching in oil or salt may be used in order to obtain the optimum quench rate.
 
Tempering:
Tools should be tempered immediately after completion of the hardening treatment. The tempering temperature may be adjusted according to the final hardness desired. Double temper at 400-750°F (200-400°C). Hold for a minimum of 2 hrs. each temper. Tempering in this temperature range provides the best corrosion resistance and wear resistance. Tempering between about 800 and 1000°F (427 and 538°C) is not recommended. All martensitic stainless steels suffer from embrittlement when tempered in this range.
For optimum stress relieving and dimensional stability, Micro-Melt 420-CW may be double tempered at 1025°F, but some loss of corrosion resistance may result.
A –100°F refrigeration treatment may be employed between the first and second tempers, if desired. Freezing treatments should always be followed by at least one temper.
The typical hardness of Micro-Melt 420-CW after hardening and tempering is 56-60 HRC.
 
Physical Properties:
QuantityValueUnit
Thermal expansion16 – 17e-6/K
Thermal conductivity16 – 16W/m.K
Specific heat500 – 500J/kg.K
Melting temperature1370 – 1400°C
Service temperature0 – 500°C
Density8000 – 8000kg/m3
Resistivity0.7 – 0.7Ohm.mm2/m
 
Thermal Properties:
PropertiesConditions
T (°C)Treatment
Thermal Conductivity (W/m-K)42.7100
 Specific Heat (J/kg-K)47750-100
 
Forging Properties:
Heat slowly to 2000/2100°F (1093/1149°C). Do not work below 1700°F (927°C). Reheat as necessary. Cool forgings slowly and anneal immediately upon cooling.
 
Stress Relieving:
Annealed Parts: Heat to 1100-1300°F (593-705°C), hold 2 hours, then furnace cool or cool in still air.
Hardened Parts: Heat to 25-50°F (15-30°C) below original tempering temperature, hold 2 hours, then furnace cool or cool in still air.
 
Normalizing:
Normalizing is not recommended.
 
Annealing:
Heat slowly to 1650°F (899°C), hold for 2 hours, cool slowly at a rate of 25°F (14°C) maximum per hour to 1000°F (538°C), then either furnace cool or cool in still air to room temperature. Typical annealed hardness will be 277 Brinell.
 
Density:
QuantityValueUnit
Density8000-8000kg/m3
 
Machinability:
The machinability of Micro-Melt 420-CW tool steel in the annealed condition may be rated between 35% and 40% of 1% carbon tool steel. Tooling providers’ recommendations for cutting fluids should be followed.
Micro-Melt 420-CW tool steel can be easily EDM’d. Use proper precautions to prevent and/or remove the “white layer.”
 
Welding:
 
Supply Cities:
Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Tuticorin, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thanjavur, Trichy, Erode, Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchipuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijayawada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.