DIN 1.2714 Steel Round Bar, DIN 1.2714 Steel Round Bar Manufacturers, DIN 1.2714 Steel Suppliers, DIN 1.2714 Stockist, DIN 1.2714 Steel Dealers, DIN 1.2714 Steel Distributors, DIN 1.2714 Wholesalers, DIN 1.2714 Steel Traders, DIN 1.2714 Steel Square Distributors, DIN 1.2714 Steel Flat Bar, DIN 1.2714 Steel Companies Near me.

Grade Introduction:

1.2714 is a German Hot work alloy steel material grade.it is shock-resisting steel. it belongs to DIN 17350 standard. Digital Grade material number W-Nr 1.2714, Metal Steel grade 56NiCrMoV7.  It is a die steel, use in extrusion molds, Hot Cast molds. like aluminum production, Aluminum cast mold. Our Tool Steel material 100 % ultrasonic tested at a good price. Small size steel products make by hot rolled, large size steel products make by forging.

Grade Application:

1.2714 cold working tool steel is for general-purpose tools and dies where greater toughness is required, but with some sacrifice of abrasion resistance.

Typically used below applications:

  • spindles,

  • forming rolls,

  • punches,

  • blanking and forming dies,

  • trimmer dies,

  • clutch parts,

  • pawls,

  • bearings,

  • chucks parts,

  • rollers,

  • knuckle pins,

  • clutch pins,

  • shear blades

Equivalent grades:

USA Germany China   Japan France  England Italy Poland  Czechia  Austria Russia Inter
DIN,WNr GB JIS AFNOR BS UNI PN CSN ONORM GOST ISO
L6 55NiCrMoV6 5CrNiMo  SKT4 55NCDV7    BH224-5   44NiCrMoV7-               KU WNL 19662 W501 5KHNM 55NiCrMoV7     
  56NiCrMoV7          56NiCrMoV7-KU WNLV 19663 W502 5KHNV  

Addition to other grades:

MS, EN1A, EN3B, EN8, EN8D, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, HCHCR, OHNS, D2, D3, H-11, H-13, CW-1, M2, M35, M42, SKD-11, P20, P20+S, P20+Ni, SCM 420, ASTM SA-36, ASTM SA-105, SAE 1018, SAE 1020, SAE 4140, SAE 8620, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE 52100, S40C, S355J2G3.

Our Supply Range: 

Price List:

People also search as:

DIN 1.2714, DIN 1.2714 Steel, DIN 1.2714 Chemical composition, DIN 1.2714 Mechanical properties, DIN 1.2714 Equivalent Grades, DIN 1.2714 Steel plate, DIN 1.2714 Steel sheet, DIN 1.2714 Manufacturers, DIN 1.2714 Suppliers, DIN 1.2714 Dealers, DIN 1.2714 Stockist, DIN 1.2714 Distributors, DIN 1.2714 Wholesalers, DIN 1.2714 Traders.

Chemical composition:

The following table shows the chemical composition of DIN 1.2714 steel:

Element C Si Mn Ni P S Cr Mo V
Content (%) 0.5 – 0.6 0.1 – 0.4 0.6 – 0.9 1.5 – 1.8 0.03 Max 0.03 Max 0.8 – 1.2 0.35 – 0.55 0.05 – 0.15

Mechanical Properties: 

Hardness         (HB) Rp 0.2 Yield Strength Rm Tensile Strength Elongation          K C V 20°C Elastic modulus
MPa ksi MPa ksi % J GPa ksi
376 1045 151 1270 184 10 40 205 29733

Hardness:

Annealing  255 HB max, Q+T: 58-38HRc, different hardness according to different Tempering temperature.

Heat treatment:

Heat treatment temperatures, rate of heating, cooling, and soaking times will vary due to factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium, and workpiece transfer facilities.

Hardening:

Hardening temperature/℃: 840~870, Quenching in oil

Tempering:

Commonly used drawing temperature/℃: 400~650;  tempering after-hardening values /MPa|400℃: 1770;  tempering after-hardening values /MPa|500℃: 1570;  tempering after-hardening values /MPa|600℃: 1320;  tempering after-hardening values /MPa|650℃: 1180

Physical Properties:

  • Density: 7.85kg/m3

  • Thermal conductivity

  • Forging ratio: 4:1 Minimum

  • Microstructure

  • Magnetic

Thermal Properties:

Thermal conductivity (°C)  20  350  700 
W/(m*K)  35.0  39.0  36.0 

Forging Properties:

For forging 1.2714 steel, Slowly Pre-heat, at Hot-working temperature/℃: 1050~850

Stress Relieving:

When tools made from 1.2714 steel are heavily machined or ground, the relief of internal strains is advisable before hardening to minimize the possibility of distortion. Stress-relieving of this grade should be done after rough machining. To stress relief, heat the component carefully to 600-650°C, allow a good soaking period, about two hours per 25mm of section. Cool in the furnace to 500°C then freely in the air. Tools may then be finish machined before hardening.

Normalizing:

Because of its air-hardening ability, 1.2714 – Hot-Work Mould Steel should not be normalized.

Annealing:

Annealing temperature/℃: 680~710; After the annealing, degree of hardness ≤HBS: 250

Density:

  • Density: 7.85kg/m3

Machinability:

The machinability of tool steel L6 is very good. It rates 90% of the machinability of the W-group water hardening low alloy steels rated 100% as a baseline.

Welding:

Stress tempering for prehardened condition.

Supply Cities:

Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Tuticorin, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thanjavur, Trichy, Erode, Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchipuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijayawada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.